Loading Port:Shanghai
Payment Terms:TT OR LC
Min Order Qty:1 m.t.
Supply Capability:350 m.t./month
epdm rubber cable:
1, 30-year professional manufacturer
2, low-smoke, halogen-free, flame retardant
3, UL and CM grade
epdm rubber cable:
1. Type and application
Type | Product | Application and Cable Specification |
GDWE1125 | 125 degree C Silane Cross-linkable Low Smoke Halogen Free Flame Retardant EPDM Compound | Used as insulation for low voltage cables, flexible cables, and rubber insulation and jacket for 105 degree C and 125 degree C cross-linkable low smoke halogen free cables Work temperature: -40 to 125 degree C |
GYJE-20 | Silane Cross-linkable EPDM Insulating Compound | Used as rubber insulation for 15 to 20 KV cables and flexible cables, and rubber insulation and jacket for 70 degree C to 125 degree C cables Work temperature: -40 to 125 degree C |
GYJE-10 | Silane Cross-linkable EPDM Insulating Compound | Used as rubber insulation for less than 10 KV cables and flexible cables, and rubber insulation and jacket for 70 degree C to 125 degree C cables Work temperature: -40 to 125 degree C |
2. Description
Silane cross-linkable EPDM rubber compound, based on EPDM and other copolymer, is produced and pelletized by special technology, adding some flame retardant, initiating agent, cross-linking agent, and some other suitable additives. This compound contains two parts A and B, which should be mixed according to suitable proportion when used. This compound has well performance of processing easily, physical properties, and cost advantage with low density.
3. Processing
The following temperature(℃) profile of extruder is recommended:
Type | Proportion of A and B | Processing Equipment | Compression ratio | L/D | Processing temp. | Cross-linkable conditions | |||||
Z 1 | Z2 | Z3 | Z4 | Head | Die | ||||||
GDWE1125 | 90:10 | It is better to use professional extruder for halogen free compound. If you use PVC extruder, the speed should be lower, reinforce cooling | 1.2~1.5:1 | 25:1~ 18:1 | 100 | 140 | 160 | 160 | 165 | 170 | Hot water or steam, based on the terms of more than 85℃, 4h/mm thickness cross-linking speed |
GYJE-20 GYJE-10 | 97:3 | Conventional PVC extruder | 2.5:1~3.5:1 | 25:1 | 110~170℃ | 180-190℃ |
method of application:
1. When you use this product, please mix A and B before put into the hopper. If you need color, the cable factory can use the polyvinylene masterbatch. The material should be used up in 8 hours after being opened and the rest can be resealed and usable within 24 hours.
2. The extruder should be cleaned after stopping with PVC material, (It is preferable if you can take apart the screws to clean.)
3. The silane cross-linkable LSZH compound should not be stayed in the extruder for a long time .If it stayed for long time, it will pre-crosslink after open the machine, which will make lumps in the surface of cable. It need to be discharged all the pre cross-linker, and then produce the cable properly.
4. To ensure the safety and fully of the cross-linking, when immersed the compound into the hot water or steam, please calculate the cross-linking time based on the terms of more than 85℃, 8h/mm thickness cross-linking speed.
5. At room temperature, the degree of cross-linking can also meet requirements after 4-10 days. The specific time can be different according to the temperature and humidity.
Note:
1. Transportation: avoid direct sunlight and weathering and machine damage
2. Convey: discharge softly, put off softly, avoid from the bursting by the stressed with the aluminum-plastic Bag.
3. Storage: it can not be landing stack. It should be put on the pallet in the clean dry storage.
4. Keep dry: When the material used, it must not be contained the outer water. Otherwise, it will seriously pre-crosslink.
5. Quality guarantee period: 6 months after manufacturing.
4. Storage and transport
Packaging:Vacuum Aluminum foil and PE membrane inside bag, and kraft outside bag.
Storage and transport: Avoiding in direct sunlight and weathering. The storage place should be clean, cool, dry, and ventilated.
5. Properties
Note: The below data is got after the compound boiled in 80 degree C water 4 hours. Natural crosslink can also be finished at proper temperature and in proper time.
NO. | Item | Units | GDWE1125 | GYJE-20 | GYJE-10 | |||
Standard Vaule | Typical Value | Standard Vaule | Typical Value | Standard Vaule | Typical Value | |||
1 | Density | g/cm3 | — | 1.35 |
| 0.9 |
| 0.88 |
2 | Tensile Strength | MPa | ≥10 | 12.0 | ≥16 | 23.0 | ≥16 | 21.0 |
3 | Elongation at break | % | ≥150 | 250 | ≥300 | 530 | ≥300 | 540 |
4 | Hardness | Shore A | — | 90 |
| 90 |
| 70 |
5 | Thermal aging |
|
|
|
|
|
|
|
Conditions: temperature | 158℃ |
|
|
|
|
|
| |
time | 168h |
|
|
|
|
|
| |
TS retention | % | ≤±30 | -11 | ≤±30 | -6 | ≤±30 | -8 | |
EB retention | % | ≤±30 | -10 | ≤±30 | -8 | ≤±30 | -7 | |
6 | Thermal prolongation |
|
|
|
|
|
|
|
200℃,0.2MPa,15min |
|
|
|
|
|
|
| |
Elongation under load | % | ≤175 | 80 | ≤175 | 70 | ≤175 | 70 | |
Permanent deformation | % | ≤15 | 0 | ≤15 | 0 | ≤15 | 0 | |
7 | Volume Resistivity | Ω·m | ≥1.0×1012 | 2.3×1013 | ≥1.0×1013 | 1.0×1014 | ≥1.0×1013 | 1.0×1014 |
8 | Dielectric Strength | MV/m | ≥20 | 28 | ≥25 | 35 | ≥25 | 32 |
9 | Resistance to thermal stress crack | h | ≥96 | pass |
|
|
|
|
10 | Resistance to environment stress crack | h | ≥96 | pass |
|
|
|
|
11 | Oxygen Index |
| ≥30 | 30 |
|
|
|
|
12 | Smoke density Flaming |
| ≤100 | 60 |
|
|
|
|
Non flaming |
| — | 180 |
|
|
|
| |
13 | Burst size of HCL | mg/g | ≤5 | 0 |
|
|
|
|
14 | PH Value |
| ≥4.3 | 5.6 |
|
|
|
|
15 | Conductivity | μS/mm | ≤10 | 0.6 |
|
|
|
|
16 | Toxicity Index |
| ≤5 | 1 |
|
|
|
|