silica fire brick
1.Stable Capability,
2.High Quality,
3.Excellent Service,
4.Competitive price
Silica fire Brick
With dense and smooth appearance, uniform corner and edge, pure color and luster and accurate size
1)Silicon oxide is above 95%.
2) Good acid erosion resistance.
3) High softening point with temperature.
4) No shrink in burn repeatedly.
5) Temperature of refractoriness under load is above 1650º C
Stable Capability, High Quality, Excellent Service, Competitive price is the most important advantage of our products
Item | BG-94 | BG-95 | BG-96A | BG-96B | |
Chemical composition | SiO2 | ≥94 | ≥95 | ≥96 | ≥96 |
Fe2O3 | ≤1.5 | ≤1.5 | ≤0.8 | ≤0.7 | |
Al2O3+TiO2+R2O |
| ≤1.0 | ≤0.5 | ≤0.7 | |
Refractoriness °C | 1710 | 1710 | 1710 | 1710 | |
Apparent Porosity% | ≤22 | ≤21 | ≤22 | ≤22 | |
Bulk Density g/cm3 | ≥1.8 | ≥1.8 | ≥1.8 | ≥1.8 | |
True Density,g/cm3 | ≤2.38 | ≤2.38 | ≤2.34 | ≤2.34 | |
Cold Crushing Strength Mpa | ≥24.5 | ≥29.4 | ≥35 | ≥35 | |
0.2Mpa Refractoriness Under Load T0.6 °C | ≥1630 | ≥1650 | ≥1680 | ≥1680 | |
Permanent Linear Change On Reheating (%)1500°CX2h | 0~+0.3 | 0~+0.3 | 0~+0.3 | 0~+0.3 | |
20-1000°C Thermal Expansich10-6/°C | 1.25 | 1.25 | 1.25 | 1.25 | |
Thermal Conductivity (W/MK) 1000°C | 1.74 | 1.74 | 1.44 | 1.44 |