Loading Port:Qingdao
Payment Terms:TT or LC
Min Order Qty:100 kg
Supply Capability:10000 kg/month
Application: | Refractory | Thickness: | 10-50mm | Width: | 300,600mm |
Length: | 900mm,600mm | Grade: | HZ (High Zirconium) | Chemical Composition: | Aluminosilicate |
Ultimate Strength (≥ MPa): | 0.5 | Working Temperature: | 1350C | Fiber Diameter: | 3-5um |
Thermal Conductivity: | -3(1000C) | Shrinkage (1800℉, 3h): | 0.085-0.180w/m.k(400-1000C) | Place of Origin: | China (Mainland) |
Model Number: | 1430C HZ | Brand Name: | Color: | Pure White | |
Density: | 260/280/300/320kg/m3 |
Packaging Detail: | carton,or according to customer's requirement |
Delivery Detail: | About 15 days |
Process:swinging technology
Excellent resistance against chemical attack
Density, 260-320kg/m3
Product Introduction:
Aluminum silicate ceramic fiber board takes ceramic fibers as the main raw materials ,After fiber processing, slag removaling,then add some organic and inorganic binder,through vacuum forming process,to be made into high-strength fiber board .Products are divided into :common,high pure ,high aluminum,zirconium type ceramic fiber board.
The ceramic fiber paper with the advantage of uniform quality , smoothly surface ,pure white color, the working temperature can be reached into 950°C-1430°C,Products with low shot content, achieving the best insulation performance,with average density, hardness, strength of the highest uniformity ,products can be turning, milling, planing, grinding, drilling, cutting, carving, etc processing. This product is hard and tough,with high strength and excellent high temperature performance and support force.
Product Features:
Low heat capacity, low thermal conductivity
Non-brittle material, good elasticity
Resistance to wind and erosion,long service life
Acoustic performance
Rigid, free support
Good anti-spalling properties
Easy to shape or cutting
High strength and excellent machinability.
Size can be accurate to ± 1mm
Product Application:
Applications that require high-temperature toughness, high strength from the load-bearing areas
For high air flow, mechanical damaging large areas of Industrial furnace wall lining, door and roof seals
Construction, fire doors, fire wall fire insulation
High-temperature pipe wall lining
High-temperature furnace insulation
High temperature gasket
Glass tank furnace insulation panels
Furnace roof insulation
Molten metal delivery system
Combustion chamber insulation
Shipping, aviation, precision industrial equipment
ITEM | PRODUCT | COM | STD | HP | HA | HZ |
Classification Temperature ºC | 1100 | 1260 | 1260 | 1360 | 1430 | |
Working TemperatureºC | <1000< p=""> | 1050 | 1100 | 1200 | 1350 | |
Color | white | white | white | white | white | |
Densitykg/m3 | 260 - 320 | 260 - 320 | 260 - 320 | 260 - 320 | 260 - 320 | |
Liner Shrinkage % After 24hours | -4 | -3 | -3 | -3 | -3 | |
1000ºC | 1000ºC | (1000ºC) | (1000ºC) | (1000ºC) | ||
Thermal conductivity w/m.k density128Kg/m3) | 0.085 (400ºC) | 0.085 (400ºC) | 0.085 (400ºC) | 0.085 (400ºC) | 0.085(400ºC) | |
0.132 (800ºC) | 0.132 (800ºC) | 0.132 (800ºC) | 0.132 (800ºC) | 0.132(800ºC) | ||
0.180 (1000ºC) | 0.180 (1000ºC) | 0.180 (1000ºC) | 0.180 (1000ºC) | |||
Tensile strength MPa (Strenth10%) | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
Chemical Composition % | Al2O3 | 44 | 46 | 47-49 | 52-55 | 39-40 |
Al2O3+SiO2 | 96 | 97 | 99 | 99 | - | |
Al2O3+SiO2+ ZrO2 | - | - | - | - | 99 | |
ZrO2 | - | - | - | - | 15-17 | |
Fe2O3 | <1.2< p=""> | <1.0< p=""> | 0.2 | 0.2 | 0.2 | |
Na2O+K2O | ≤0.5 | ≤0.5 | 0.2 | 0.2 | 0.2 | |
Size(mm) | Specification:600X400X10-50,900X600X20-50,other according to customer's requirement |