1)High Temperature Burnt Slide Plate
This product adopts tabular alumina, carbonaceous material and zirconia-containing material as main raw materials, adds in high performance antioxidants, uses phenolic resin as binder, formed under high-pressure and burned under high temperature. Mainly used in large and medium-sized ladle.
Physical and chemical properties:
Chemical and Physical Properties | Al-C Slide Gate Plate | Al-Zr-C Slide Gate Plate | ||||||
LQSP-70 | LQSP -75 | LQSP -80 | LQSP -85 | LQSP -86 | LQSP -70 | LQHSP-75 | LQHSP -77 | |
Al2O3,% | 70 | 75 | 80 | 85 | 86 | 70 | 75 | 77 |
C,% | 7 | 7 | 5 | 5 | 4 | 7 | 7 | 7 |
ZrO2,% | - | - | - | - | - | 6 | 6 | 2.5 |
A.P.,% max | 10 | 10 | 10 | 10 | 7 | 10 | 10 | 10 |
B.D.,g/cm3 | 2.8 | 2.9 | 2.9 | 3.0 | 2.95 | 3.00 | 3.05 | 2.90 |
C.C.S., MPa min | 65 | 70 | 100 | 100 | 100 | 110 | 115 | 100 |
2) Low Temperature Burnt Slide Plate
Tabular alumina, zirconia-containing material and spinel as major raw materials, adding in special metal, using phenolic resin as binder, being burned under low temperature during producing process. Mainly used in small and medium-sized ladles.
Physical and chemical properties:
Chemical and Physical Properties | Low Temperature Burnt Slide Gate Plate | ||||
LQLTSP-70 | LQLTSP-75 | LQLTSP-80 | LQLTSP-85 | LQLTSP-86 | |
Al2O3,% min | 70 | 75 | 80 | 85 | 86 |
C,% | ≥5 | ≥5 | ≥5 | ≥4 | 4 |
A.P.,% max | 10 | 10 | 10 | 8 | 7 |
B.D.,g/cm | 2.9 | 2.95 | 3.00 | 3.10 | 2.95 |
C.C.S., MPa ≥ | 90 | 90 | 100 | 120 | 100 |
3) Unburned Slide Plate
Without being burned, tar impregnated and distilled, simple processing. Mainly used in small and medium-sized ladles.
Physical and chemical properties:
Chemical and Physical Properties | Al-C Slide Gate Plate | ||||
LQUSP-70 | LQUSP-75 | LQUSP-80 | LQUSP-85 | LQUSP-86 | |
Al2O3,% | 70 | 75 | 80 | 85 | 86 |
C,% | 7 | 7 | 5 | 5 | 4 |
A.P.,% max | 10 | 10 | 8 | 10 | 7 |
B.D. g/cm3 min | 2.8 | 2.9 | 3.0 | 3.0 | 2.95 |
C.C.S., MPa min | 65 | 70 | 100 | 100 | 100 |