Specifications
.cold working tool steel 1.2210 /DIN 115CrV3, AISI L2.ISO9001:.quality guaranted
.Manufacturer,UT% before delivery
Quick Details
| Standard: | AISI,ASTM,BS,DIN,GB,JIS | Place of Origin: | Shanghai China (Mainland) | Brand Name: | Unite Steel |
| Technique: | Hot Rolled | Application: | Tool Steel Bar | Alloy Or Not: | Is Alloy |
| Special Use: | Mold Steel | Type: | Alloy Steel Bar |
Specifications
Round bar:
Diameter : 1mm-2000mm
Square bar:
Size: 50mm * 50mm-600mm *600mm
STEEL GRADES:115CrV3
Chemical composition % of the ladle analysis of grade 115CrV3
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | V(%) | Ti(%) |
| 1.10-1.25 | 0.15-0.30 | 0.20-0.40 | Max 0.030 | Max 0.030 | 0.50-0.80 | 0.07-0.12 | |||
| W(%) | N(%) | Cu(%) | Co(%) | Pb(%) | B(%) | Nb(%) | Al(%) | Ta(%) | Other(%) |
Mechanical properties of grade 115CrV3
Technological properties of grade 115CrV3
Hardness and heat treatment specification of grade 115CrV3
| Annealing hardness HBS | Cold pull hardness HBS | Preheating temperature °C | Quenching temperature °C | Holding time min | Hardening medium | Temper temperature °C | After tempering hardness ≥HRC | |
| salt-bath furnace | controlled atmosphere furnace | |||||||
| 235 | 262 | 788 | 1191 | 1204 | 5~15 | air cooling | 522 | 60 |
| Steel plate/Sheet thickness / mm | σb MPa | σs ≥/MPa | δ Samples from the standard for 50 mm (2 in) | 180 ° of cold bending test | |
| longitudinal | horizontal | ||||
| Hot-rolled/Cold rolling:5 - 150 | 520 | 415 | 16~18 | 2a | 3.5a |
| Note: (1) listed in the table apex diameter (d), to steel thickness (a) multiples said. (2) in the ASTM A6 standard specified scope can meet any additional conditions. (3) from the standard for 50 mm (2 in). Mechanical properties Mechanische Eigenschaften Caracteristiques mecaniques ReH Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d’elasticite minimale Rm Tensile strength / Zugfestigkeit / Resistance a la traction A Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal J Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc | |||||