Submerged Arc Welding Flux 

1.Product No: JN-HJ107  

2.Color:Grey blue

3.Mesh:8-60 (2.5-0.3mm)

4.Package: 25Kgs per PP woven bag

5.MOQ:1 Ton

 

Fit: GB/T17854-1999 F308-H0Cr21Ni10 F308L-H00Cr21Ni10 F316L-H00Cr19Ni12Mo2 

 

1.JN-HJ107 is a kind of smelting-type non-Mn mid-Si and mid-F flux.

 

2.Grain Size:10-60 (2.0-0.3mm) or 8-40 (2.5-0.45mm) meshes.

 

3.Current:direct current.

 

4.Performance:anti-porosity and anti-cracking.

 

Usage:  

1.Excellent clad layers can be gained when it is used in the build-up welding in conjunction with appropriate welding wires or solder strips, such as HOCr21Ni10 (AWS ER308), HOCr20Ni10Ti(AWS ER321), HOOCr21Ni10 (AWS ER308L), HOOCr24Nb, HOCr16Mn16.

 

2.for build-up welding of petrochemical equipments' corrosion-proof layers, stainless clad layers and pressure vessels. 

 

3.In conjunction with HOCr16Mn16, it can be used in the build-up welding of the track switch of high manganese steel (Mn13) and welding of Nb-contained stainless steel, etc.

 

Performance of Surfacing Layers :  

It can be used in the transition-layer welding in conjunction with HOOCr26Ni12 and in the build-up welding of 50mm-thick 18MnMoNb steel plate in conjunction with HOOCr21Ni10 as the surface-layer welding band.

 

Chemical Compositions: 

 

  AL2O3 +MnO

 

 CaO+MgO

 

  TiO2 +SiO2

 

  CaF2

 

 others

 

   S  P

 

        24~30

 

     14~21

 

      26~30

 

 20~26

 

  ≤ 10

 

 ≤ 0.05

 

Cautions: 

 1. Flux must be baked for 2 hours under the temperature of 250~300°c before welding.  

 2. The iron rust, oil contamination and moisture on the weldment must be removed.