| Place of Origin: | Henan, China (Mainland) | Shape: | Powder | Material: | Clay,Alumina magnesia,Bauxite-mullite,Corundun |
| SiO2 Content (%): | 15%-30% | Al2O3 Content (%): | 45%-90% | MgO Content (%): | 4.4% |
| CaO Content (%): | 1.2-3.2% | Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°) | CrO Content (%): | Appropriate |
| SiC Content (%): | Appropriate | Model Number: | Customer's Requirement, refractory castable | Brand Name: | cnbm |
| Compressive strength 1000°C: | 40-74Mpa | Compressive strength 1500°C: | 43-150Mpa | Bending Strength 1000°C: | 11-19Mpa |
| Bulk density(g/cm3): | 2.3 | Bending Strength 1500°C: | 13-23Mpa | Reheating linear change 1000°C: | -0.02-+0.08 |
| Reheating linear change 1500°C: | +0.10-+0.62 | Max Service temperature °C ≥: | 1650 | Color: | White,Yellow,Grey Green etc |
| Packaging Details: | 1.25kg/Bag 2.As your demands |
| Delivery Detail: | 30 days after down deposit |
Specifications&Data
What is the details of our steel fiber reinforced refractory castable?
Steel fiber reinforced refractory castable is a special castable which is added steel fiber into the castable,can improve the toughness,mechanical strength,thermal shock resistance and spalling resistance.
What is the Feature of Our steel fiber reinforced refractory castable?
1.High mechanical strength,
2.Good thermal shock resistance,
3.Good toughness and anti-stripping,
4.High refractoriness,
5.Tiny linear variation,no cracking,
6.Resistant to scour and erosion,
7.Good volume stability under high temperature.
What is the Applications of our steel fiber reinforced refractory castable?
Steel fiber reinforced refractory castable is mainly used in heat treatment furnace,heating furnace,soaking pit furnace,tundish slag dam weir,seconclary refining and the catalytic cracking unit etc key part of kiln furnace and thermal equipment.
What is the Technique Data of our steel fiber reinforced refractory castable?
Item | Fire clay | High alumina | Corundum | |
Chemical Composition % | Al2O3 ≥ | 45 | 75 | 90 |
CaO ≤ | 1.0 | 1.0 | 1.0 | |
Bulk density g/cm3 | 110°C,24h | 2.40 | 2.70 | 3.15 |
1350°C,3h | 2.35 | - | - | |
1500°C,3h | - | 2.65 | 3.10(1550°C) | |
Reheating linearchange % | 1350°C,3h | ±0.5 | - | - |
1500°C,3h | - | ±0.5 | ±0.5(1550°C) | |
Bending Strength MPa | 110°C,24h | 6 | 7 | 7 |
1350°C,3h | 8 | - | - | |
1500°C,3h | - | 10 | 10(1550°C) | |
Compressive strength MPa | 110°C,24h | 40 | 40 | 40 |
1350°C,3h | 75 | - | - | |
1500°C,3h | - | 85 | 90(1550°C) | |
Service temperature °C ≥ | 1500 | 1550 | 1650 | |