Silica brick for coke oven

Loading Port:Qingdao

Payment Terms:TT OR LC

Min Order Qty:100 PCS

Supply Capability:50000 PCS/month

The silica bricks for HBS
Silica fire brick for coke oven
High density silica fire brick
Semi-silics fire brick for coke oven

1.Silica brick manufature.
2.High refractoriness under load.
3.High heat conductivity.
4.Good thermal shock resistance.

Tech Data

Silica brick for glass furnace
Item:		GF-96A	GF-96B	GF-95A	GF-95B
SiO 2		≥96	≥96	≥95	≥95
Fe 2 O 3		≤0.8	≤1.0	≤1.2	≤1.2
Apparent porosity %		≤22(24)
Cold Crushing Strength MPa	Brick below20KG	≥35(30)
	Brick ≥20KG	≥30(25)
Refractoriness under load ºC		≥1680	≥1670	≥1660	≥1650
True density g/cm ³		≤2.34	≤2.34	≤2.35	≤2.35

Silica brick for coke oven
Item:	CO-94A	CO-94B
SiO2: %	≥94	≥94
Al 2 O 3 : %	≤ 1.5	≤ 1.5
Fe2O3: %	≤ 1.5	≤ 1.5
Refractoriness under load 0.2Mpa	≥ 1650ºC	≥ 1650ºC
Apparent porosity: %	≤ 22	≤ 24
Bulk density: g/cm ³	≤ 2.34	≤ 2.35
Cold crushing strength: MPa	≥30	≥25
Permanent linear change % (1450ºC ×2h)	0~0.2	0~0.2
Thermal expansion(1000ºC)	≤1.28	≤1.30

Silica brick for hot blast furnace
Item	HBF-95
SiO2	≥ 95
Al2O3	≤ 1.0
Fe2O3	≤1.3
Apparent porosity %	≤22(24)
Cold crushing strength MPa	≥45(35)
Remaining quarts %	≤1.0
Refractoriness under load ºC	≥1650
Creep(0.2Mpa ×1550ºC×50h) %	≤0.8
Thermal expansion coefficient (1000ºC) %	≤1.25
Apparent density g/cm ³	≤2.32