I. Type andapplication
Type | Product | Application and Cable Specification |
5601N | PVC insulating compound for UL standard at 60℃ | Used for wires and cables which according with UL standard, such as UL62, 83, 758, 1581 and etc |
5801N | No lead PVC insulating compound for UL standard at 80℃ | Used for wires and cables which according with UL standard, such as UL62, 83, 758, 1581 and etc |
5901N | No lead PVC insulating compound for UL standard at 90℃ | Used for wires and cables which according with UL standard, such as UL62, 83, 758, 1581 and etc |
5501N | No lead PVC insulating compound for UL standard at 105℃ | Used for wires and cables which according with UL standard, such as UL62, 83, 758, 1581 and etc |
II. Productdescription
PVC insulatingcompound for UL standard wires and cables, based on PVC resin, is made intogranula by mixing, plastification and granulation with adding plasticizer,stabilizing agent, flame retardant and etc. The products meet various specialrequirements, such as different hardness, UV stable, environment friend (RoHs,REACH, PAHs, chlorinated alkanes free, phthalate free, and etc.), sub-shine and fog surface, low temperatureresistant, PS/ABS transfer proof, rodent-repellent, termite-repellent, andtransparent, and etc.
III. Processing
It is recommended that compound should beprocessed with common extruder having a minimum L/D ratio of 20.
The following temperature(℃)profile of extruder is recommended:
Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Head | Die |
Temperature ℃ | 140 | 160 | 170 | 175 | 180 | 175 |
IV. Storageand transport
Packaging：25kg/bag， PE membrane inside bag and Kraft outsidebag.
Storage and transport: Avoiding in directsunlight and weathering. The storage place should be in clean, cool, dry, andventilated conditions.
V. Properties
Table
Item | Unit | Standard Value | |||
5601N | 5801N | 5901N | 5501N | ||
Tensile Strength | ≥MPa | 15.0 | 15.0 | 15.0 | 15.0 |
Elongation at Break | ≥ % | 150 | 150 | 150 | 150 |
Impact Brittleness Temperature | ℃ | -15 | -15 | -15 | -15 |
Volume Resistivity, at 20℃ | ≥Ω﹒m | 1.0×1011 | 1.0×1011 | 1.0×1011 | 1.0×1011 |
Volume Resistance at working temperature | ≥Ω﹒m | 1.0×108 | 1.0×108 | 1.0×108 | 1.0×108 |
Dielectric Strength | ≥MV/m | 20 | 20 | 20 | 20 |
Hot Deformation | ≤ % | 40 | 40 | 30 | 30 |
Thermal Stability Time at 200℃ | ≥min | 60 | 80 | 100 | 120 |
Thermal Aging (UL oven) |
|
|
|
|
|
Aging Temperature | ℃ | 100±1 | 100±1 （113±1） | 121±1 | 136±1 |
Aging Time | h | 168 | 240 （168） | 168 | 168 |
Retention on Tensile Strength | ≥ % | +85 | +85 | +85 | +85 |
Variation on Elongation at Break | ≥ % | +65 | +65 | +65 | +65 |