PRIMER PAINT paints

RED OXIDE PRIMER

TYPE

Antirust paint based on alkyd resins with red oxide pigments.

USES

Antirust under coat for steel.

CHARACTERISTICS

1. Very fast drying.

2. Good adhesion.

3. Excellent resistance to water and weathering.

4. Reality low cost.

GLOSS

Flat

COLOR

Red

WEIGHT

Above 1.3 kg/L

VISCOSITY (25 °C)

90 - 100 KU

DRYING TIME (25 °C)

Set-to-touch

Dry hard

0.5 hrs.

2 hrs.

OPTIMUM FILM THICKNESS

Wet

Dry

90μ(microns)

40μ(microns)

OVERCOATING INTERVALS (25°C)

Min. 6 hrs.

NON-VOLATILE CONTENT

Above 65%

THINNER

Toluene

THINNING RATE

70~%(depends on tools used)

APPLICATION METHOD

Airless Spray, Brush, Roller.

NOTE

1. Moisture, grease, rust, dirt and loose paints film on

substrate must be removed. As a result, paint

performance can be ensured.

2. Before application, stir paint evenly. When paint is

too thick, thinner can be added within specified

quantity

3. Application should avoid the following environment:

rainy day; substrate is damp by dew; temperature is

above 40°C or below 10°C.

4. Subsequent coat has to wait until paint films of

preceding coat completely dry off.