1.Introduction of Polyvinyl Chloride (PVC) waterproofing membrane:
Polyvinyl Chloride (PVC) waterproofing membrane is a new polymer waterproof membrane which is made from polyvinyl chloride resin, and mixed with plasticizer,filler, antioxygen, ultraviolet absorber and other auxiliaries. DHK-8100 adopts automatic mixing of raw material, double-screw extruder and delicate three-roller calender equipment in the PVC membrane production. DHKchem PVC waterproof membrane features dimensional stability and high tensile strength, being a best choice for many civil and industrial project.
2.Physical data of Polyvinyl Chloride (PVC) waterproofing membrane:
No | Item | I | II | |
1 | Tensile strength/ Mpa | 8.0 | 12.0 | |
2 | Fracture elongation / % ≥ | 200 | 250 | |
3 | Heating flexibility / % ≤ | 3.0 | 2.0 | |
4 | Cold bending | -20°C No leaking | -25°C No leaking | |
5 | Water impermeability | Water impermeable | ||
6 | Binding property with cutting (N/mm) | 3.0/ breaking membrane | ||
7 | Hot air ageing | Appearance | No craze, no bubble, no cohering, hole | |
Tension strength % | ±25 | ±20 | ||
Fracture elongation changing rate | ||||
Cold bending % | -15°C No leaking | -20°C No leaking | ||
8 | Chemistry corrosion resistance | Tension strength % | ±25 | ±20 |
Fracture elongation changing rate | ||||
Cold bending % | -15°C No leaking | -20°C No leaking | ||
9 | Phytotrons accelerating ageing | Tension strength % | ±25 | ±20 |
Fracture elongation changing rate | ||||
Cold bending % | -15°C No leaking | -20°C No leaking | ||
10 | Note: no considering phytotrons accelerating ageing. | |||
3.Chatacteristics of Polyvinyl Chloride (PVC) waterproofing membrane:
Excellent performance in aging resistance, service life of 20 years for exposed use, and 50 years for non-exposed application.
Easy installation and hot-air welding seam, environmental friendly.
High tension, perfect elongation, perfect heating resistance.
Excellent jointing, it can be fused with base as a whole after heating jointing.
High permeability, chilling material and moisture can be expelled easily.
High UV resistance , corrosion resistance and erosion resistance.
High cold flexibility (-20°C).
Surface can reflect UV. The temperature on the surface is low due to little absorbing heat.
4.Application of Polyvinyl Chloride (PVC) waterproofing membrane:
Colorful polymer PVC waterproof membrane can variously be used on the roof of building, underground building, tunnel, dam, pool, sewage treatment works, and garbage disposal facilities. It also can be suitable to any requirement of all kinds of technological practice & different grade of roof waterproof and underground constructions waterproof.