MS Galvanized Steel Round Bars

Loading Port:Tianjin,China

Payment Terms:TT or LC

Min Order Qty:25 Tons m.t.

Supply Capability:5000 Tons Per Month m.t./month

Product Description:

Specifications of Galvanized Steel Round Bar

1. Invoicing on theoretical weight or actual weight as customer request

2. Length: 6m, 9m, 12m as following table

galvanzied round bar

Size: 5.5mm-500mm

Zinc thickness:30-86μm

Grade: Q195,A3,Q235,10#,20#,35#,45#,60#,80#,20Mn,45Mn,50Mn,65Mn,S50C,K40,T8,T10,Q345A,Q345B,Q345C,Q345D,Q345E,16MnCR4,12Cr1MoV, 20Cr,35Cr,40Cr,27SiMn,15CrMo,20CrMo,35CrMo,42CrMo,45CrMo

Standard:

GB/T14975-2002 GB/T14976-2002 GB13296-91

GB9948-88 ASTM A312 ASTM A213

ASTM A269 ASTM A511

diameter (mm)	area of section (cm2)	theoretical weight (kg/m)	diameter (mm)	area of section (cm2)	theoretical weight (kg/m)
5	0.1963	0.154	45	15.90	12.48
5.6	0.2463	0.193	48	18.10	14.21
6	0.2827	0.222	50	19.64	15.42
6.3	0.3117	0.245	53	22.06	17.32
7	0.3848	0.302	56	24.63	19.33
8	0.5027	0.395	60	28.27	22.19
9	0.6359	0.499	63	31.17	24.47
10	0.7854	0.617	65	33.18	26.05
11	0.9503	0.746	70	38.48	30.21
12	1.131	0.888	75	44.18	34.68
13	1.327	1.04	80	50.27	39.46
14	1.539	1.21	85	56.75	44.55
15	1.767	1.39	90	63.62	49.94
16	2.011	1.58	95	70.88	55.64
17	2.270	1.78	100	78.54	61.65
18	2.545	2.00	105	86.59	67.97
19	2.835	2.23	110	95.03	74.60
20	3.142	2.47	120	113.10	88.78
21	3.464	2.72	125	122.72	96.33
22	3.801	2.98	130	132.73	104.20
24	4.524	3.55	140	153.72	120.84
25	4.909	3.85	150	176.72	138.72
26	5.809	4.17	160	201.06	157.83
28	6.158	4.83	170	226.98	178.18
30	7.069	5.55	180	254.47	199.76
32	8.042	6.31	190	283.53	222.57
34	9.079	7.13	200	314.16	246.62
36	10.18	7.99	210	346.36	271.89
38	11.34	8.90	220	380.13	298.40
40	12.57	9.87	240	452.39	355.13
42	13.85	10.87	250	490.88	385.84

Material Specifications of Galvanized Steel Round Bar:

Standard	Name	Grade	chemistry								Remark	Strength (Mpa)
			C	Mn	Si	Cr	Ni	Cu	S	P
GB/T701-2008	Common Carbon Structure Steel	Q195	≤0.12	0.25-0.50	0.30				0.040	0.035	GB/T14292-93 GB/T702-2008	≥195
		Q215	0.09-0.15	0.25-0.60	0.30				0.045	0.045		≥215

		Q235	0.12-0.20	0.30-0.70	0.30				0.045	0.045		≥215

		Q275	0.14-0.22	0.40-1.00	0.30				0.045	0.045		≥235

Galvanzied Round Bar

Usage & Applications of Galvanized Steel Round Bar

(1).used for metallurgical, mechanical, electrical construction field

(2).used for ships, military (armored) Construction

(3).used for outside engineering, machine tool base, automobile rear of products

Packaging & Delivery of of Galvanized Steel Round Bar

1. Packing: it is nude packed in bundles by steel wire rod

2. Bundle weight: not more than 3.5MT for bulk vessel; less than 3 MT for container load

3. Marks:

Color marking: There will be color marking on both end of the bundle for the cargo delivered by bulk vessel. That makes it easily to distinguish at the destination port.

Tag mark: there will be tag mark tied up on the bundles. The information usually including supplier logo and name, product name, made inChina, shipping marks and other information request by the customer.

If loading by container the marking is not needed, but we will prepare it as customer request.

4. Transportation: the goods are delivered by truck from mill to loading port, the maximum quantity can be loaded is around 40MTs by each truck. If the order quantity cannot reach the full truck loaded, the transportation cost per ton will be little higher than full load.

5. Delivered by container or bulk vessel

Galvanzied round bar steel

Production flow of of Galvanized Steel Round Bar

A typical hot-dip galvanizing line operates as follows:

Steel is cleaned using a caustic solution. This removes oil/grease, dirt, and paint.
The caustic cleaning solution is rinsed off.
The steel is pickled in an acidic solution to remove mill scale.
The pickling solution is rinsed off.
A flux, often zinc ammonium chloride is applied to the steel to inhibit oxidation of the cleaned surface upon exposure to air. The flux is allowed to dry on the steel and aids in the process of the liquid zinc wetting and adhering to the steel.
The steel is dipped into the molten zinc bath and held there until the temperature of the steel equilibrates with that of the bath.
The steel is cooled in a quench tank to reduce its temperature and inhibit undesirable reactions of the newly formed coating with the atmosphere.