Loading Port:Tianjin
Payment Terms:TT OR LC
Min Order Qty:1000 m.t.
Supply Capability:100000 m.t./month
1. Structure of Metallurgical Coke of Met Coke(For the 2015 purchase season) Description：
Coke reactivity and carbon dioxide, oxygen and water vapor on the ability of chemical reaction, CRI = (G0, G1 / G0 x 100% (note: coke G0 - test sample weight, g, G1 - coke after reaction sample weight, g).Coke after coke strength after reaction is refers to the response under the action of thermal stress and mechanical force and resistance to fracture and wear ability.Coke in the blast furnace ironmaking, casting iron and fixed bed gasification process, will react with carbon dioxide, oxygen and water vapor.Due to the reaction of coke with oxygen and water vapor and carbon dioxide reaction similar laws, so most countries use coke reaction with carbon dioxide features assess coke reactivity.China standard (GB/T4000-1996) provides for coke reactivity and strength after reaction test method.Its practices is to make coke at high temperature and the reaction of carbon dioxide, and then determining reaction after coke weightlessness rate and mechanical strength.
CRI and strength after reaction coke reactivity of CSR repeatability r shall not exceed the following values:
CRIr 2.4% or less
CSR: 3.2% or less
The coke reactivity and strength after reaction of the test results are shown parallel arithmetic mean of test results.
2. Main Features of the Metallurgical Coke of Met Coke(For the 2015 purchase season) ：
• Quality assurance
• Mutual benefit
• Preferential price
• Various choice
3. Metallurgical Coke of Metallurgical Coke(For the 2015 purchase season) Images:
4. Metallurgical Coke of Metallurgical Coke(For the 2015 purchase season) Specification:
Guarantee | Rejection | |
Total Moisture (As received basis) | 5% max | |
Ash (dry basis) | 12.5% max | > 13.5% |
Volatile Matter (dry basis) | 1.5% max | > 1.8% |
Sulphur (dry basis) | 0.65% max | > 0.75% |
Phosphorus (dry basis) | 0.035% max | > 0.045% |
M10 | 7% max | > 9% |
M40 | 84% min | ＜82% |
CSR | 64% min | ＜62% |
CRI | 26% max | > 28% |
Size 30-90 mm | 90% min | |
+90 mm | 5% max | > 8% |
-30mm | 5% max | > 8% |
5. FAQ
What are coke's main physical properties?
on the relative density of density, coke, coke porosity, thermal conductivity for the heat capacity of coke, coke, coke, coke ignition temperature, coke thermal expansion coefficient of thermal stress and coke, coke shrinkage rate, coke resistivity permeability, etc.
The average heat capacity is 0.808 kj/(KGK) (100 ℃), 1.465 kj/(KGK) (1000 ℃)
Thermal conductivity is 2.64 kj/(MHK) (room temperature), 6.91 kj/(MHK) (900 ℃);
Ignition temperature (air) is 450-650 ℃.