1. Structure of Metallurgical Coke of Coke Strength after Reactivity 62 Description：
Coke is made by high temperature metallurgical coke for blast furnace smelting, casting and gasification. Occurring in the process of coking after recovery and purification of coke oven gas is a high calorific value of fuel, is an important industrial raw material in organic synthesis.
Bituminous coal under the condition of the air, heated to 950-950 ℃, after drying, pyrolysis, molten, bonding, solidification and contraction phase resulting coke, this process is called high temperature coking (high temperature carbonization).Made by high temperature metallurgical coke for blast furnace smelting, casting and gasification.Occurring in the process of coking after recovery and purification of coke oven gas is a high calorific value of fuel, is an important industrial raw material in organic synthesis.
2. Main Features of the Metallurgical Coke of Coke Strength after Reactivity 62：
• Quality assurance
• Mutual benefit
• Preferential price
• Various choice
3. Metallurgical Coke of Coke Strength after Reactivity 62 Images:
4. Metallurgical Coke of Coke Strength after Reactivity 62 Specification:
Parameters | Guarantee | Rejection |
Total Moisture (As received basis) | 5% max | |
Ash (dry basis) | 12.5% max | > 13.5% |
Volatile Matter (dry basis) | 1.5% max | > 1.8% |
Sulphur (dry basis) | 0.65% max | > 0.75% |
Phosphorus (dry basis) | 0.035% max | > 0.045% |
M10 | 7% max | > 9% |
M40 | 84% min | ＜82% |
CSR | 65% min | ＜63% |
CRI | 25% max | > 27% |
aSize 30-90 mm | 90% min | |
+90 mm | 5% max | > 8% |
-30mm | 5% max | > 8% |
5. FAQ
Foundry coke is dedicated to cupola molten iron. Coke is the main fuel of cupola molten iron. Its role is hot metal melting furnace charge and overheating, support stock column maintain its good air permeability. As a result, coke blocks should have large, low reactivity, low porosity, with sufficient impact crushing strength, ash content and low sulfur content.