1.Chemical Composition of Low Breakage Rate Grinding Media Ball Made in China with the Top Quality Steel and High Hardness
Material | C | Mn | Si | Cr | S | P | V |
50MN | 0.48-0.56 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 | |
60MN | 0.57-0.65 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 | |
65MN | 0.60-0.70 | 0.90-1.20 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 | |
75Mn | 0.72-0.92 | 0.17-0.37 | 0.17-0.37 | 0.4-0.6 | ≤0.035 | ≤0.035 | |
75MnCr | 0.70-0.85 | 0.7-0.8 | 0.17-0.37 | 0.2-0.7 | ≤0.03 | ≤0.03 | |
75SiMn | 0.70-0.90 | 0.7-1.2 | 0.4-0.8 | ≤0.25 | ≤0.03 | ≤0.03 | |
Wear-resistant Alloy | 0.5-0.65 | 0.4-1.0 | 1.4-1.8 | 0.9-1.2 | ≤0.03 | ≤0.03 | 0.1-0.2 |
Material | C | Si | Cr | Mn | S | P |
Cr-22-32% | 2.0-2.8 | ≤1.0 | 22-32 | 0.5-2.0 | ≤0.06 | ≤0.08 |
Cr-17-22% | 2.0-2.8 | ≤1.0 | 17-22 | 0.5-2.0 | ≤0.06 | ≤0.08 |
Cr-15-17% | 2.2-3.0 | ≤1.0 | 15-17 | 0.5-2.0 | ≤0.06 | ≤0.08 |
Cr-11-14% | 2.2-3.2 | ≤1.0 | 11-14 | 0.5-2.5 | ≤0.06 | ≤0.08 |
Cr-5-10% | 2.1-3.2 | ≤1.2 | 5-10 | 0.5-1.5 | ≤0.06 | ≤0.08 |
Cr-1.5-3% | 2.2-3.5 | ≤1.2 | 1.5-3 | 0.5-1.5 | ≤0.06 | ≤0.08 |
2. Hardness of Low Breakage Rate Grinding Media Ball Made in China with the Top Quality Steel and High Hardness
1A | 2A | 3A | 45 | 65 | |
Superficial | >60HRC | >60HRC | >60HRC | >58HRC | >60HRC |
Volumetric | >58HRC | >60HRC | >60HRC | >55HRC | >60HRC |
3.Feature of Low Breakage Rate Grinding Media Ball Made in China with the Top Quality Steel and High Hardness
1) In general, grinding steel ball has high hardness: surface hardness to 58-65 HRC, volume hardness of 56-65 HRC
2) impact toughness high: impact toughness more than 12 J / cm2.
3) broken rate is low: the actual broken rate is not higher than 0.5%.
4) loss of grinding forged steel ball round rate is low.