Loading Port:China Main Port
Payment Terms:TT or LC
Min Order Qty:10 Metric Tons watt
Supply Capability:3000 Metric Tons per Month watt/month
Appearance: White or Gray Granule
LDPE is the low density version of PE. This has less hardness, stiffness and strength compar
|
Product |
LDPE |
|
Resin Properities |
Test Result |
|
Melt Indexg/10min |
7~8 |
|
Densityg/ 12cm3' |
>0.922 |
|
Tensile-strength |
Mpa9 |
|
Elongationat break |
500% |
|
Softening pointVicat> |
83°C |
|
Physical Properties |
Test Method |
Nominal Value |
Unit | |
|
Density |
ISO 1183 |
0.921 |
g/cm3 | |
|
Melt Mass-Flow Rate (MFR) |
ISO 1133 |
1.9 |
g/10min | |
|
Hardness |
|
|
| |
|
Shore Hardness (shore D) |
ISO 868 |
45 |
| |
|
Mechanical Properties |
|
|
| |
|
Tensile Modulus |
ISO 527-2 |
175 |
MPa | |
|
Tensile Strength |
Yield, |
ISO 527-2 |
9.0 |
MPa |
|
Break, |
13.0 |
MPa | ||
|
Tensile Strain(Break) |
ISO 527-2 |
850 |
% | |
|
Modulus of Elasticity |
Internal Method |
250 |
MPa | |
|
Thermal |
|
|
| |
|
Vicat Softening Temperature |
ISO 306/A50 |
89.0 |
°C | |
|
Melting Temperature (DSC) |
DIN 53765 |
108 |
°C | |
|
Peak Crystallization Temperature (DSC) |
DIN 53765 |
97.0 |
°C | |
|
Heat of Fusion |
DIN 53765 |
110 |
J/g | |
|
Electrical |
|
|
| |
|
Volume Resistivity |
ASTM D257 |
8.5E+15 |
ohm •cm | |
|
Dielectric Strength |
ASTM D149 |
30.0 |
kV/mm | |
|
Dielectric Constant (60Hz) |
ASTM D150 |
2.20 |
% | |
|
Dissipation Factor (60 Hz) |
ASTM D150 |
0.00050 |
| |