Composition: This product is a highly corrosion-resistant protective primer made of inorganic silicate, antirust pigment with zinc powder and many kinds of imported additives.
Application: It is suitable as the protective primer on the surface of various steel structures in steel structure buildings, steel structure bridges, high-speed railway stations, engineering equipment, port and dock machinery, etc., which are in harsh corrosive environments and require a long protective life, providing excellent adherence ability and anti-rust protection effect.
Features: Excellent antirust performance, tough paint film, good adhesion to the substrate. Good resistance to oil and solvent, easy to spray. Good temperature resistance, with long-term temperature resistance of 400℃. Small cutting ablation area, good welding performance.
Specifications:
Color | Glossiness | Recommended Dry Film Thickness | Theoretical Coating Rate | Actual Coating Rate | Apply Method |
Gray | Flat | 50-75 µm | 5.26 m²/kg at 50 µm dry film thickness | Appropriate loss factors are allowed | Free air spraying brush coating and rolling coating are limited to small area repair |
Drying time: Surface drying time 5 minutes, hard drying time 7-10 minutes. The actual drying time would be decided according to the specific temperature conditions.
Construction parameters:
Construction Methods | Units | High-Pressure Airless Spraying | Air Spraying | Brush/Roller Coating |
Spray gun aperture | mm | 0.43-0.58 | 1.5-2.5 | —— |
Spraying pressure | Kg/cm2 | 150-200 | 3-4 | —— |
Dilution | % | 0-10 | 5-15 | —— |