| Application: | Heat Insulation | Thickness: | Customizable | Width: | Custonizable |
| Length: | Customizable | Grade: | HP (High Pure) | Chemical Composition: | 72%-75% |
| Ultimate Strength (≥ MPa): | ≥0.05 | Working Temperature: | 1600C, 1700C, 1800C | Fiber Diameter: | 3~5um |
| Thermal Conductivity: | 0.12-0.2 w/m.k (600-1000C) | Shrinkage (1800℉, 3h): | -3% (24h) | Place of Origin: | China (Mainland) |
| Model Number: | JY-CF-B3 | Brand Name: | Density (volume weight) (kg/m3): | 300-600 |
| Packaging Detail: | Standard Export Packaging |
| Delivery Detail: | Within 5-10 days |
Product Description
High Temperature Heating Insulation Ceramic Fiber Board for Industrial Kiln
Heat insulation ceramic fiber board is high performance insulation products manufactured from ceramic fiber (or with alumina fiber) and binders, with unique shot removing and vacuum forming process, provide excellent high temperature stability, extra low thermal conductivity, high compressive strength.
Features:
♦ Low heat storage and low thermal conductivity;
♦ High compression strength;
♦ Non –fragile materials and good toughness;
♦ Accurate dimension and good paleness;
♦ Structure homogeneity and easy machining;
♦ Easy to install;
♦ Continual production, even fiber with stable property;
♦ Excellent heat stability and thermal shock resistance.
Technical Data:
Sheet 1:
Type | Common | Standard | High Pure | High aluminum | Zircon | |
Classification temperature (°C) | 1100 | 1260 | 1260 | 1360 | 1430 | |
Working temperature (°C) | ≤1000 | 1050 | 1100 | 1200 | 1350 | |
Color | White | Pure White | Pure White | Pure White | Pure White | |
Density (kg/m3) | 260-320 | 260-320 | 260-320 | 260-320 | 260-320 | |
Shrinkage on heating (%) (Temperature 24 hours, density as 320kg/m3) | -4 | -3 | -3 | -3 | -3 | |
Thermal conductivity of various temperatures (w/m.k) (density 285kg/m3) | 0.085 (400°C) (800°C) (1000°C) | 0.085 (400°C) (800°C) (1000°C) | 0.085 (400°C) (800°C) (1000°C) | 0.085 (400°C) 0.132 (800°C) (1000°C) | 0.085 (400°C) (800°C) (1000°C) | |
Compressive strength (Mpa) | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
Chemical composition (%) | AL2O3 | 44 | 46 | 47-49 | 52-55 | 39-40 |
AL2O3+SIO2 | 96 | 97 | 99 | 99 | - | |
AL2O3+SIO2+ZrO2 | - | - | - | - | 99 | |
ZrO2 | - | - | - | - | 15-17 | |
Fe2O3 | <1.2< span=""> | <1.0< span=""> | 0.2 | 0.2 | 0.2 | |
Na2O+K2O | ≤0.5 | ≤0.5 | 0.2 | 0.2 | 0.2 | |
Dimensions (mm) | Common Specifications: 600*400*10-50; 900*600*10-50; 1200*500*10-50; 1200*1000*10-50; 1000*600*10-50mm | |||||
Sheet 2:
Type | JINYU-1400 | JINYU-1600 | JINYU-1800 | |
Temperature | 1400°C | 1600°C | 1800°C | |
Density(Kg/m3) | 300-600 | 450 | 550 | |
Chemical Components | Al2O3 | 50 | 68 | 85 |
Al2O3+SiO2 | 99 | 99.5 | 99.8 | |
Fe2O3 | 0.2 | ~ | ~ | |
Application:
High-temperature steady | Verity high-temperature industrial furnace backing heat insulation |
Low heat conductivity | Ceramics kiln, mechanic and metallurgy heating furnace, thermal treatment furnace and others industrial furnace and hot face internal lining Low heating quantity High-temperature block-fire and flame-insulated |
Easy-mechanic processing | Kiln door, kiln car and dilatation joint etc insulation material |
Tidy surface | Glass kiln insulation |
FAQ:
Q1: Why buy Materials & Equipment from OKorder.com?
A1: All products offered by OKorder.com are carefully selected from China's most reliable manufacturing enterprises. Through its ISO certifications, OKorder.com adheres to the highest standards and a commitment to supply chain safety and customer satisfaction.
Q2: How do we guarantee the quality of our products?
A2: We have established an advanced quality management system which conducts strict quality tests at every step, from raw materials to the final product. At the same time, we provide extensive follow-up service assurances as required.
Q3: What other products does OKorder offer?
A3: We offer a full range of refractory bricks, mortar, cement, ceramic fiber products, and more.