| Application: | Heat Insulation | Thickness: | 10-50mm,10-50mm (made as your requirement) | Width: | 1200/1000/900/600mm |
| Length: | 1000/600/400mm | Grade: | ST (Standard),ST (Standard) /HA (High Aluminum) | Chemical Composition: | AL2O3,SiO2 |
| Ultimate Strength (≥ MPa): | 40Mpa | Working Temperature: | 1260 | Fiber Diameter: | 3~5μm |
| Thermal Conductivity: | 0.32 W/m.k | Shrinkage (1800℉, 3h): | -3 | Place of Origin: | (Mainland) |
| Model Number: | yy-03 | Brand Name: | Density: | 250-400kg/m3 | |
| Al2O3+SIO2: | 97% | Type: | Ceramic fiber board |
| Packaging Detail: | by carton. |
| Delivery Detail: | 10 days |
high aluminium ceramic fiber board
1.Thermal conductivity low
2.Excellent breaking strength
3.ISO certification
Ceramic fiber board
Type | Ceramic fiber board |
Thickness | 10-50mm (made as your requirement) |
Grade | ST (Standard) /HA (High Aluminum) |
Ultimate Strength (≥ MPa) | 40Mpa |
Length | 1200/1000/900/600mm |
Width | 1000/600/400mm |
Color | Pure white |
Shrinkage (1800°F, 3h) | -3 |
Chemical Composition | AL2O3,SiO2 |
Thermal Conductivity | 0.32 W/m.k |
Density | 250-400kg/m3 |
Fiber Diameter | 3~5μm |
Al2O3+SIO2 | 97% |
Thermal Conductivity | 0.32 W/m.k |
Working Temperature | 1260 |
Min. Order | 21 m3 (1x20’FCL) |
Shipment | Within 15days after receive trial order |
Application | Refractory |
Supply Ability | 300,000 Pieces/Month |
photo |
|
High aluminium ceramic fiber board index
Type List Item | Common | Standard | High-purity | High- aluminium | Zirconic | |
Classification Temperature(°C) | 1100 | 1260 | 1260 | 1360 | 1430 | |
Working Temperature(°C) | 1000 | 1050 | 1100 | 1200 | 1350 | |
Color | White | White | White | White | White | |
Volume Density(kg/m³) | 96,128 | 96,128 | 96,128 | 128,160 | 128,160 | |
Permanent Linear Contrative(%) (insulation 24 hours volume density 128kg/m³) | -4 (1000°C) | -3 (1000°C) | -3 (1100°C) | -3 (1250°C) | -3 (1350°C) | |
Each Heat Surface Temperature Of The Thermal Conductivity(W/M.K) (density 128kg/m³) | 0.09(400°C) 0.176(800°C) | 0.09(400°C) 0.176(800°C) | 0.09(400°C) 0.176(800°C) 0.22(1000°C) | 0.132(600°C) 0.22(1000°C) | 0.76(600°C) 0.22(1000°C) | |
Tensile Strength (Mpa) (density 128kg/m³) | 0.08—0.12 | 0.08—0.12 | 0.08—0.12 | 0.08—0.12 | 0.08—0.12 | |
Chemical Composition(%) | AI2O3 | 44 | 46 | 47-49 | 52-55 | 39-40 |
AI2O3+SIO2 | 96 | 97 | 99 | 99 | - | |
AI2O3+SIO2+ZrO2 | - | - | - | - | 99 | |
ZrO2 | - | - | - | - | 15-17 | |
Fe2O3 | <1.2 | <1.0 | 0.2 | 0.2 | 0.2 | |
Na2O+K2O | <0.5 | < 0.5 | 0.2 | 0.2 | 0.2 | |
Product Size(mm) | 7200*610*10-50; | |||||