Loading Port:China main port
Payment Terms:TT OR LC
Min Order Qty:25 m.t.
Supply Capability:2000 m.t./month
Raw material: Natural ore and its extract or other synthetic materials.
Refractory brick features:
1.Export more than 20 countries;
2.Accurate delivery time;
3.Professional technical service;
4.Most bricks in stock.
Refractory brick Process:
Raw material to factory→ checkout→ burdening→stirring→mixing→taking out the raw material→transfer
→enter into mould→press machine extrusion→going out the mould→stoving→going into the furnace→firing
→stopping burn→cooling→open the furnace door→going out the furnace→checkout→packing→qualified product
→putting in storage→sale
High Alumina Refractory Brick Physical and Chemical Index : | ||||||
Item | Properties | |||||
LZ-80 | LZ-75 | LZ-65 | LZ-55 | LZ-48 | ||
Al2O3 (%) | 80 | ≥75 | ≥65 | ≥55 | ≥48 | |
Refractoriness (°C ) | ≥1790 | ≥1790 | ≥1790 | ≥1770 | ≥1750 | |
Bulk density (g/cm3) | 2.65 | 2.5 | 2.45 | 2.4 | 2.3 | |
Softening temperature under load (°C ) | 1530 | ≥1520 | ≥1500 | ≥1470 | ≥1420 | |
Linear changes on reheating (%) | 1500°CX2H | 0.1 | 0.1 | 0.1 | 0.1 | |
-0.4 | -0.4 | -0.4 | -0.4 | |||
1450°CX2H | 0.1 | |||||
-0.4 | ||||||
Apparent porosity (%) | 22 | ≤23 | ≤23 | ≤22 | ≤22 | |
Cold crushing strength (Mpa) | 55 | ≥50 | ≥45 | ≥40 | ≥35 | |
Application | steel furnace, glass furnace, sodium silicate furnace, ceramic shuttle kiln, cement rotary kiln, blast furnace, electric furnace, blast furnace and reverberatory furnace. |
Other Refractory Product:
Item | Product | Reference Index | Application |
1 | Fire Clay Brick | 1.Al2O3:30-48%; 2.Refractoriness:1580-1750°C; 3.Refractoriness under load:1300-1400°C; 4.Bulk density:2.0-2.2g/cm3. | 1.Glass furnace, 2.Heating furnace, 3.Hot blast stove, 4.Blast furnace, 5.Metal melting furnace, 6.Bolier, 7.Pizza oven, 8.All industrial furnace. |
2 | Low Porosity Fire Clay Brick | 1.Al2O3:41-45%; 2.Refractoriness:≥1750°C; 3.Refractoriness under load:>1500°C; 4.Bulk density:2.3-2.37g/cm3; 5.Apparent porosity:12-15% | 1.Glass industry, 2.Steel industry, 3.Chemical industry. |
3 | High Alumina Brick | 1.Al2O3:48-80%; 2.Refractoriness:≥1790°C; 3.Refractoriness under load:1300-1400°C; 4.Bulk density:2.3-2.65g/cm3. | 1.Glass furnace, 2.Heating furnace, 3.Heat treatment furnace, 4.Blast furnace, 5.Metal melting furnace, 6.Electric furnace, 7.Pizza oven, 8.All industrial furnace. |
4 | Fused Cast Zirconia Corundum Block | 1.Al2O3:40-50%; 2.ZrO2:32-41%; 3.SiO2:13-17%; 4.Exudation temperature of glass phase: 1080-1400°C; 5.Refractoriness under load:1400-1450°C; 4.Bulk density:3.4-3.95g/cm3. | 1.Flat glass furnace, 2.Glass tube furnace, 3.Float glass furnace, 4.Glass bottle furnace, 5.Sodium silicate furnace, 6.Ceramic frit furnace, 7.Glass melting furnace. |
5 | Sintered Azs Refractory Brick | 1.ZrO2:18-30%; 2.Al2O3:48-70%; 2.Refractoriness:1770-1790°C; 3.Refractoriness under load:1600-1680°C; 4.Bulk density:2.8-3.4g/cm3. | 1.Glass furnace, 2.Sodium silicate furnace, 3.Ceramic Frit furnace, 4.Metallurgical furnace. |
6 | Sintered Zircon Firebrick | 1.ZrO2:64%; 2.SiO2:34%; 2.Refractoriness:1790°C; 3.Refractoriness under load:1620°C; 4.Bulk density:3.5-3.7g/cm3. | 1.Glass furnace, 2.Sodium silicate furnace, 3.Ceramic Frit furnace, 4.Metallurgical furnace. |
7 | Sintered Zirconia-mullite Brick | 1.ZrO2:18-25%; 2.Al2O3:60-67%; 2.Refractoriness:1790°C; 3.Refractoriness under load:1650°C; 4.Bulk density:2.9-3.0g/cm3. | 1.Glass furnace, 2.Sodium silicate furnace, 3.Ceramic Frit furnace, 4.Ladle lining. |
8 | Sillimanite Refractory Brick | 1.Al2O3:>60%; 2.SiO2:37%; 3.Refractoriness:1790°C; 4.Refractoriness under load:1450-1510°C; 5.Bulk density:2.2-2.4g/cm3. | 1.Glass furnace, 2.Float glass furnace, 3.Feeding machine, 4.Drawing machine. |
9 | Sintered Mullite Fire Brick | 1.Al2O3:64-80%; 2.Fe2O3:0.5-1.2%; 3.Refractoriness:1790°C-1810°C; 4.Refractoriness under load:1560-1700°C; 5.Bulk density:2.45--2.75g/cm3 | 1.Glass furnace, 2.Float glass furnace, 3.Feeding machine, 4.Drawing machine. |
10 | Silica Brick | 1.SiO2:95-96%; 2.Refractoriness:1710°C; 3.Refractoriness under load:1650-1680°C; 4.Bulk density:1.85-1.9g/cm3. | 1.Glass furnace, 2.Coke oven, 3.Hot blast stove. |
11 | Magnesia Fire Brick | 1.MgO:92-97%; 2.CaO:2-2.5%; 3.SiO2:1-4%; 4.Refractoriness under load:1600-1700°C; 5.Bulk density:2.88-3.0g/cm3. | 1.Glass Furnace, 2.Cement kiln, 3.Metallurgical furnace, 4.Steel making electric furnace 5.Flat furnace. |