Loading Port:China Main Port
Payment Terms:TT or LC
Min Order Qty:1 Ton m.t.
Supply Capability:1000 Tons per Month m.t./month
1,HDPE/LDPE/LLDPE resin
2,Virgin & Recycled
3.Film grade,blow grade,injection grade ect.
4,Manufacturer & Free sample
HDPE:
| HDPE cable material
Property |
Unit |
Typical Value |
| Mass density | g/cm 3 | 0.941-0.959 |
| Melt flow Rate(190 centidegree /2.16kg) | g/10min | ≤1.0 |
| Tensile yield strength | MPa | ≥19.0 |
| Flexural modulus | Mpa | ≥965 |
| Elongation@ break | % | ≥400 |
| Impact Embrittlement temperature | centidegree | MAX -118 |
| Dielectric Constant | 100KHZ | 2.32 |
| 1MHZ | 2.31 | |
| Loss Tangent | 100KHZ | MAX 0.0001 |
| 1MHZ | MAX 0.0001 | |
| Volume resistivity | OHM-CM | MIN 1x10 15 |
| Application |
Mainly used for the production of high toughness of the telephone,cable insulation material | |
LDPE:
|
Physical Properties |
Test Method |
Nominal Value |
Unit | |
|
Density |
ISO 1183 |
0.921 |
g/cm3 | |
|
Melt Mass-Flow Rate (MFR) |
ISO 1133 |
1.9 |
g/10min | |
|
Hardness |
|
|
| |
|
Shore Hardness (shore D) |
ISO 868 |
45 |
| |
|
Mechanical Properties |
|
|
| |
|
Tensile Modulus |
ISO 527-2 |
175 |
MPa | |
|
Tensile Strength |
Yield, |
ISO 527-2 |
9.0 |
MPa |
|
Break, |
13.0 |
MPa | ||
|
Tensile Strain(Break) |
ISO 527-2 |
850 |
% | |
|
Modulus of Elasticity |
Internal Method |
250 |
MPa | |
|
Thermal |
|
|
| |
|
Vicat Softening Temperature |
ISO 306/A50 |
89.0 |
°C | |
|
Melting Temperature (DSC) |
DIN 53765 |
108 |
°C | |
|
Peak Crystallization Temperature (DSC) |
DIN 53765 |
97.0 |
°C | |
|
Heat of Fusion |
DIN 53765 |
110 |
J/g | |
|
Electrical |
|
|
| |
|
Volume Resistivity |
ASTM D257 |
8.5E+15 |
ohm •cm | |
|
Dielectric Strength |
ASTM D149 |
30.0 |
kV/mm | |
|
Dielectric Constant (60Hz) |
ASTM D150 |
2.20 |
% | |
|
Dissipation Factor (60 Hz) |
ASTM D150 |
0.00050 |
| |