TECHNICAL PROPERTIES OF GRAPHITE ELECTRODE
1.Physical and chemical index
Item | Unit | RP | HP | UHP | ||||
250-400 | 450-800 | 300-400 | 450-700 | 300-400 | 450-700 | |||
Electric Resistivity | Electrode | μΩ.m | 7.5-8.6 | 7.5-8.8 | 5.5-6.8 | 5.5-7.0 | 4.6-6.0 | 4.8-6.2 |
Nipple | 4.5-5.5 | 4.0-5.0 | 3.5-4.5 | |||||
Bending Strength | Electrode | MPa | ≥8.0 | ≥11.0 | ≥11.0 | |||
Nipple | ≥15.0 | ≥16.0 | ≥18.0 | |||||
Elastic Modulus | Electrode | GPa | ≤9.0 | ≤11.0 | ≤13.0 | |||
Nipple | ≤13.0 | ≤14.0 | ≤15.0 | |||||
Bulk Density | Electrode | g/cm3 | 1.55-1.65 | 1.63-1.73 | 1.65-1.75 | |||
Nipple | 1.70-1.75 | 1.73-1.80 | 1.75-1.82 | |||||
Ash | Electrode | % | ≤0.3 | |||||
Nipple | ||||||||
CTE (100-600)℃ | Electrode | 10-6/℃ | 2.00-2.50 | 1.80-2.00 | 1.30-1.50 | |||
Nipple | 1.50-1.80 | 1.50-1.80 | 1.20-1.40 |
2.Recommended current carrying capacity
Nominal Diameter (mm) | RP | HP | UHP | ||||
Current Carrying Capacity | Current Density | Current Carrying Capacity | Current Density | Current Carrying Capacity | Current Density | ||
in | mm | A | A/cm2 | A | A/cm2 | A | A/cm2 |
12 | 300 | 1000-13000 | 14-18 | 13000-174000 | 17-24 | 15000-22000 | 20-30 |
14 | 350 | 13500-18000 | 14-18 | 17400-24000 | 17-24 | 20000-30000 | 20-30 |
16 | 400 | 18000-23500 | 14-18 | 21000-31000 | 16-24 | 25000-40000 | 19-30 |
18 | 450 | 22000-27000 | 13-17 | 25000-40000 | 15-24 | 32000-45000 | 19-27 |
20 | 500 | 25000-32000 | 13-16 | 30000-48000 | 15-24 | 38000-55000 | 18-27 |
22 | 550 | 32000-40000 | 13-16 | 35000-55000 | 14-22 | 42000-64000 | 17-26 |
24 | 600 | 35000-41000 | 13-15 | 41000-61000 | 14-21 | 50000-73000 | 17-25 |
28 | 700 | 39000-48000 | 10-12 | 55000-82000 | 14-21 | 67000-99000 | 17-25 |
32 | 800 | 43000-54000 | 8-10 | / | / | / | / |
TOLERANCCES OF ELECTRODE DIAMETERS AND LENG THES (MM)
Nominal Diameter | Actual Diameter | Length | |||
in | mm | max | min | Black surface min | |
12 | 300 | 307 | 302 | 299 | 1800/2000 |
14 | 350 | 357 | 352 | 349 | 1800/2000/2200 |
16 | 400 | 409 | 403 | 400 | 1800/2000/2200 |
18 | 450 | 460 | 454 | 451 | 1800/2000/2200 |
20 | 500 | 511 | 505 | 502 | 2000/2200/2400 |
22 | 550 | 562 | 556 | 553 | 2000/2200/2400 |
24 | 600 | 613 | 607 | 604 | 2200/2400/2700 |
28 | 700 | 714 | 708 | 705 | 2400/2700 |
29 | 800 | 815 | 809 | 806 | 2700/3000 |
SIZE OF TAPER-THREAD NIPPLES AND SOCKETS(MM)
Nominal Length | Standard Deviation | Deviation of the short scale length | ||
1800 | +100 | -100 | -100 | -275 |
2000 | +100 | -100 | -100 | -275 |
2200 | +100 | -100 | -100 | -275 |
2400 | +100 | -100 | -100 | -275 |
2700 | +150 | -150 | -150 | -300 |
3000 | +150 | -150 | -150 | -300 |
FINE-GRAIN SPECIALTY GRAPHITE FXG-1
Physical and chemical index
Item | Unit | Guarantee Value | Typical Value |
Max Grante Size | mm | 0.8 | 0.8 |
Bulk Density | g/cm3 | ≥1.70 | 1.73 |
Specific Resistance | μΩ.m | ≤8.5 | 7.5 |
Bending Strength | MPa | ≥10.0 | 11.0 |
Compressive Strength | MPa | ≥24.0 | 27.0 |
Thermal Conductivity | W/(m.k) | ≥120 | 150 |
CTE (100-600)℃ | 10-6/℃ | ≤2.5 | 2.2 |
Ash Content | % | ≤0.3 | 0.09 |
FINE-GRAIN SPECIALTY GRAPHITE FXG-2
Physical and chemical index
Item | Unit | Guarantee Value | Typical Value |
Max Grante Size | mm | 0.8 | 0.8 |
Bulk Density | g/cm3 | ≥1.73 | 1.76 |
Specific Resistance | μΩ.m | ≤8.0 | 7.0 |
Bending Strength | MPa | ≥12.0 | 12.5 |
Compressive Strength | MPa | ≥31.0 | 34.0 |
Thermal Conductivity | W/(m.k) | ≥130 | 160 |
CTE (100-600)℃ | 10-6/℃ | ≤2.5 | 2.1 |
Ash Content | % | ≤0.3 | 0.09 |
MEDIUM-GRAIN SPECIALTY GRAPHITE FCP
Physical and chemical index
Item | Unit | Guarantee Value | Typical Value | Guarantee Value | Typical Value | Guarantee Value | Typical Value |
Max Grante Size | mm | 2 | 2 | 4 | 4 | 8 | 8 |
Bulk Density | g/cm3 | ≥1.58 | 1.60 | ≥1.57 | 1.58 | ≥1.56 | 1.58 |
Specific Resistance | μΩ.m | ≤11.5 | 10.5 | ≤11.5 | 10.5 | ≤12.5 | 11.5 |
Bending Strength | MPa | ≥6.0 | 6.5 | ≥6.5 | 7.0 | ≥7.0 | 7.5 |
Compressive Strength | MPa | ≥18.0 | 18.5 | ≥17.5 | 18.0 | ≥16.0 | 17.0 |
Modulus of Elasticity | GPa | ≤9.3 | 7.5 | ≤9.3 | 7.5 | ≤9.3 | 7.0 |
CTE (100-600)℃ | 10-6/℃ | ≤2.5 | 2.4 | ≤2.5 | 2.4 | ≤2.5 | 2.4 |
Ash Content | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 | ≤0.3 | 0.09 |
MEDIUM-GRAIN SPECIALTY GRAPHITE FCG-1
Physical and chemical index
Item | Unit | Guarantee Value | Typical Value | Guarantee Value | Typical Value | Guarantee Value | Typical Value |
Max Grante Size | mm | 2 | 2 | 4 | 4 | 8 | 8 |
Bulk Density | g/cm3 | ≥1.70 | 1.75 | ≥1.69 | 1.73 | ≥1.68 | 1.72 |
Specific Resistance | μΩ.m | ≤8.5 | 7.5 | ≤8.5 | 7.5 | ≤9.5 | 8.5 |
Bending Strength | MPa | ≥9.0 | 9.5 | ≥9.5 | 10.0 | ≥10.0 | 12.5 |
Compressive Strength | MPa | ≥30.0 | 31.0 | ≥29.0 | 30.0 | ≥30.0 | 31.0 |
Modulus of Elasticity | GPa | ≤12.0 | 9.5 | ≤12.0 | 9.5 | ≤12.0 | 9.0 |
CTE (100-600)℃ | 10-6/℃ | ≤2.5 | 2.3 | ≤2.5 | 2.3 | ≤2.5 | 2.3 |
Ash Content | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 | ≤0.3 | 0.09 |
FAQ
What is the consumption of your Electrode?
The comsumption of Our Electrode can be below 1.0kg/mt, and the everage is 0.5kg/mt.
What is the reason of the problem of broken?
There are several reasons, such as: Amperage is too high, the connection is not good, etc.