Dia0.75’’-Dia6’’ Forged Steel Grinding Ball with B2 or 65Mn Material with High Hardness and Good Wear Resistant
1. Detail Specifications for Dia0.75’’-Dia6’’ Forged Steel Grinding Ball with B2 or 65Mn Material with High Hardness and Good Wear Resistant
Diameter: 20mm-150mm(0.75''-6'')
Hardness: HRC60-HRC65
Breakage Rate<0.5%
Impact Toughness>12J/cm2
Endurance Test>10000times
Certification: ISO9001:2008, SGS, etc
2. Chemical Composition for Dia0.75’’-Dia6’’ Forged Steel Grinding Ball with B2 or 65Mn Material with High Hardness and Good Wear Resistant
Brand | Material | C | Mn | Si | Cr | S | P |
CMAX-1 | 50MN | 0.48-0.56 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
CMAX-2 | 60MN | 0.57-0.65 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
CMAX-3 | 65MN | 0.60-0.70 | 0.90-1.20 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
CMAX-4 | 75Mn | 0.72-0.92 | 0.70-1.20 | 0.17-0.37 | 0.4-0.6 | ≤0.035 | ≤0.035 |
CMAX-5 | 75MnCr(B2) | 0.70-0.85 | 0.7-0.8 | 0.17-0.37 | 0.2-0.7 | ≤0.03 | ≤0.03 |
CMAX-6 | 75SiMn | 0.70-0.90 | 0.7-1.2 | 0.4-0.8 | ≤0.25 | ≤0.03 | ≤0.03 |
CMAX-7 | Wear-resistant Alloy | 0.5-0.65 | 0.4-1.0 | 1.4-1.8 | 0.9-1.2 | ≤0.03 | ≤0.03 |
3. Technical Parameter for Dia0.75’’-Dia6’’ Forged Steel Grinding Ball with B2 or 65Mn Material with High Hardness and Good Wear Resistant
Brand | Impact Test AK.J/cm2 | Endurance Test Times(5m) | Surface Hardness | Core Hardness |
CMAX-1 | ≥12 | ≥10000 | ≥56 | ≥48 |
CMAX-2 | ≥13 | ≥10000 | ≥58 | ≥50 |
CMAX-3 | ≥15 | ≥12000 | ≥60 | ≥50 |
CMAX-5 | ≥17 | ≥12000 | ≥60 | ≥52 |
CMAX-6 | ≥16 | ≥12000 | ≥60 | ≥50 |
CMAX-7 | ≥17 | ≥12000 | ≥60 | ≥54 |