The details of our Steel

1. Produce Standard: as the GB, AISI, ASTM, SAE, EN, BS, DIN, JIS Industry Standard

 

2. Produce processes: Smelt Iron -EAF smelt Billet  - ESR smelt Billet -Hot rolled or forged get the  steel round bar and  plate

 

3. Heat treatment:

Normalized / Annealed / Quenched+Tempered

 

4. Quality assurance:

All order we can received  Third party inspection, You can let SGS, BV,.. and others test company test and inspect our products before Goods shipping.


Product information

 

1.ChemicalComposition(%)

 

 carbon:0.43-0.50    Silicon:0.10-0.35   Manganese: 0.60-0.90

2.Equivalent Grades

 SAE1045,AISI C1045,S45C,C45

3.Form&Size

1)1045 carbon Steel round bars, flat/square bars,plates,sheets.

2)AISI 1045 carbon steel Size Available(Length can be customized)

4.Round bar

16mm-690mm Dia

5. Typical Mechanical Properties 

Tensile strength Mpa:640   Yield strength Mpa:410      Elongation in 50% mm %:22      Impact lzod J:170-210   Hardness:HB 187 / HRC 10

6.Machining

  AISI 1045 steel has good machinability in normalized as well as the hot rolled condition. Based on the recommendations given by the machine manufacturers, operations like tapping, milling, broaching, drilling, turning and sawing etc. can be carried out on AISI 1045 steel using suitable feeds, tool type and speeds.

7.Welding

AISI 1045 steel is readily welded when correct procedure is followed.

Welding AISI 1045 steel in through-hardened, tempered and flame or induction hardened condition is not recommended.

Low hydrogen electrodes are preferred for welding AISI 1045 steel.

The workpiece is

Pre-heated at 200°C–300°C (392°F - 572°F)

Maintained at the same temperature during welding

Cooled slowly using sand, ashes etc and

Stress relieved at 550°C - 660°C (1022°F - 1220°F).

8.Related Specifications

W.Nr 1.0503 C45   W.Nr 1.1191 CK45   AISI C1045   ASTM A29/A29M-91 1045    SAE 1045     UNS G 10450

9.HeatTreatment

Annealing:Heat to 800°C-850°C hold until temperature is uniform throughout the section,and cool in furnace.

Hardening:Heat to 800°C-850°C hold until temperature is uniform throughout the section,soak for 10-15 minutes per 25mm of section,and quench in water or brine.or Heat to 830°C -860°C soak as above and quench in oil.Temper immediately while still hand warm.

Tempering:Re heat to 400°C-650°C as required,hold until temperature is uniform throughout the section,soak for 1 hour per 25mm of section,and cool in still air.   

10.Quality Certificate

1)Grade,Size,Quantity in Number & Weight
2)Heat Number
3)Chemical Composition
4)Hardness
5)Ultrasonic Test Report.