Loading Port:China main port
Payment Terms:TT OR LC
Min Order Qty:25 m.t.
Supply Capability:2000 m.t./month
| Place of Origin: | Shanxi, China (Mainland) | Shape: | Block | Material: | Alumina Block |
| SiO2 Content (%): | 5-19% | Al2O3 Content (%): | 75-89% | Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°) |
| CrO Content (%): | None | SiC Content (%): | None | Model Number: | 78,80,83,85,86,87,88,89 |
| Brand Name: | Jialun | Fe2O3: | 2%max | K2O+Na2O: | 0.25-0.4% |
| CaO+MgO: | 0.4-0.6% | Bulk Density: | 2.8-3.30 |
| Packaging Details: | 25 kg pvc bag and 1 mt big bag |
| Delivery Detail: | within 10 days after receipt your advance payment |
Introduction of calcined bauxite
Calcined bauxite is one of the principal ore of aluminum.
Calcined bauxite contains hydrous aluminum oxides and aluminum hydroxides, formed through the laterization of aluminous rocks in tropical and subtropical areas .
Calcined bauxite is obtained by calcining (heating)superior grade bauxite at high temperature (from 85OC to 1600C) .this can removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57%to 58% in raw bauxite, calcined bauxite has an alumina content of 75% to 90%.
Specifications of Calcined bauxite
Grade | AL2O3 | SIO2 | FE2O3 | TIO2 | K2O+Na2O | CaO+MgO | Bulk density |
HX75 | 75min | ≤17 | ≤3.0 | ≤4.0 | ≤0.3 | ≤0.5 | ≥2.70 |
HX80 | 80min | ≤12 | ≤3.0 | ≤4.0 | ≤0.3 | ≤0.5 | ≥2.80 |
HX85 | 85min | ≤8 | ≤2 | ≤4.0 | ≤0.3 | ≤0.5 | ≥3.00 |
HX86 | 86min | ≤7 | ≤2 | ≤4.0 | ≤0.3 | ≤0.5 | ≥3.10 |
HX87 | 87min | ≤6 | ≤2 | ≤4.0 | ≤0.3 | ≤0.5 | ≥3.20 |
HX88 | 88min | ≤5 | ≤1.8 | ≤4.0 | ≤0.25 | ≤0.5 | ≥3.25 |
HX90 | 90min | ≤3 | ≤1.8 | ≤4.0 | ≤0.25 | ≤0.5 | ≥3.3 |
Moisture(max) | 0.50% | ||||||
Usage of Calcined bauxite
1.Aluminium industry.
2.Precision casting.
3.Refractory industry.
4.Silicic acid aluminium firefibre
5.Mixed with magnesium oxide,it can be an nice bonding agent,especially for pouring entire steel teeming ladle lining
6.Manufacture bauxite cement,grinding abrasives.ceracmic industry,and chemical industry for making aluminium compounds