Loading Port:China main port
Payment Terms:TT OR LC
Min Order Qty:1000 pc
Supply Capability:10000000 pc/month
| Place of Origin: | Jiangsu, China (Mainland) | Shape: | Brick | Material: | Alumina Cement |
| SiO2 Content (%): | 18 | Al2O3 Content (%): | 49 | MgO Content (%): | 3 |
| CaO Content (%): | 4 | Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°) | CrO Content (%): | 0.6 |
| SiC Content (%): | 0.8 | Model Number: | fq036 | Brand Name: | cnbm |
| Packaging Details: | Plywood tray |
AZS firebrick
1)-The different content of ZrO2 led to three model:
| Item | Index | |||
| 33# | 35# | 40# | ||
| Chemical Composition(%) | Al2O3 | 49 | 49 | 49 |
| ZrO2 | 32.0-34.5 | 35.0-37 | 40.0-42.0 | |
| SiO2≤ | 15.5 | 14 | 13 | |
| Fe2O3≤ | 0.1 | 0.1 | 0.1 | |
| TiO2≤ | 0.05 | 0.05 | 0.05 | |
| Na2O≤ | 1.5 | 1.4 | 1.3 | |
| Physical Composition | Apparent Porosity(%) | 2 | 1.5 | 1.3 |
| Bulk Density(g/m³) | 3.8 | 3.89 | 4.12 | |
| Cold Crushing Strength(MPa) | 350 | 350 | 350 | |
| Refractorlness(°C) | 1710 | 1710 | 1730 | |
| 0.2MPa Softening temp. Under load(°C) | >1700 | >1700 | >1700 | |
| Exudation temp. of Glass Phase(°C) | >1400 | >1420 | >1430 | |
| Corrosion Resistance of Glass Melt (mm/24h) | 1.3 | 1.2 | 1.1 | |
| Thermal Expansion(%) | 0.8 | 0.8 | 0.8 | |
| Glass Phase(%) | 20 | 19 | 18 | |
| Bulk Density(g/m³) | PT.QX | 3.4 | 3.45 | 3.55 |
| ZWS | 3.6 | 3.65 | 3.9 | |
| WS | 3.7 | 3.78 | 3.92 | |