With excellent high temperature performance and spalling resistance,it is used for middle
temperature area of regenerator of glass tank.
Al2O3% ≥ | ZrO2% ≤ | A·P % ≤ | B·D g/cm3 ≥ | C·C·SMPa ≥ | 0.2MPaR·U·L℃ ≥ | T·S·R (1100℃ ≥ | ||
ANTI—SPALLING HIGH ALUMINA BRICKS | ||||||||
JJYRS-70 | 70 | 6-7 | 25 | 2.55 | 45 | 1470 | 20 | |
NEW TYPE ANTI—SPALLING HIGH ALUMINA BRICKS | ||||||||
JJYRS-76 | 76 | 25 | 2.5 | 55 | 1500 | 25 | ||
refractory ladle lining brick
1) Good thermal shock resistance
2) High-temperature endurable
3) Good thermal insulation
Description:
1. Good acid stability
2. Good thermal performance
3. Good thermal shrinkage
4 Good resistance to abrasion and corrosion
Advantage:
Fire brick is refers to the Al2O3 content is 30% ~ 40% aluminum silicate.Clay brick is made of soft clay and 50% and 50% of hard clay grog, ingredients required by certain granularity, after forming, drying, burning under the high temperature of 1300 ~ 1400 ℃.Clay brick belongs to the weak acid refractory products, can resist acid slag and the erosion of acid gases, the alkali resistance ability is a bit poor. Clay brick has good thermal shrinkage.