Grade: | HZ (High Zirconium) | Application: | Liners Of Industrial Furnace | Thickness: | 25/50 mm |
Width: | 610/600 mm | Length: | 7200/3600 mm | Chemical Composition: | 35% Al2O3+46.7% SiO2+16% ZrO2 |
Working Temperature: | 1300 | Fiber Diameter: | 2.6 | Thermal Conductivity: | 0.23 |
Density (kg/m³ ): | 128 | Model Number: | 1425 | Brand Name: | |
Place of Origin: | Color: | white |
Packaging Detail: | carton/woven bag |
Delivery Detail: | 15 days after receipt of pre-payment |
NATI Ceramic Fiber Blanket is made from long special ceramic fiber, formed by special strong double surface needling
Introduction
NATI Ceramic Fiber Blanket is made from long special ceramic fiber, formed by special strong double surface needling, without any binder ,increasing inter-weaving and tensile strength, so that NATI ceramic fiber blanket own good stability under any working temperature.
Characteristics
*Good springiness for fiber
*Excellent strength and resistance to blowing
*Excellent chemical stability, resistance to erosion
*Low thermal conductivity
*Low thermal shrinkage
*Excellent sound absorption
Typical Applications
*Filling insulation and joint sealing
*Back-up lining for industrial furnaces
*Fireproof materials for construction
*High temperature materials for filtration *
Raw materials for further producing, such as modules
Physical & Chemical Data
Description | 1000 NATI Ceramic Fiber Blanket | 1260 NATI Ceramic Fiber Blanket | 1425 NATI Ceramic Fiber Blanket | 1500 NATI Ceramic Fiber Blanket | 1600 NATI Ceramic Fiber Blanket |
Classification temperature( ℃) | 1000 | 1260 | 1425 | 1500 | 1600 |
Melting point( ℃) | 1760 | 1760 | 1800 | 1900 | 2000 |
Color | White | White | White | Green-blue | White |
Average fiber diameter (um) | 2.6 | 2.6 | 2.8 | 2.65 | 3.1 |
Fiber length (mm) | ~250 | ~250 | ~250 | ~150 | ~400 |
Density for fiber (Kg/ m3) | 2600 | 2600 | 2800 | 2650 | 3100 |
Shot content ( > 212um) (%) | 12 | 12 | 12 | ||
Thermal conductivity rate Kcal/mh℃ (W/mK) ,ASTM C201 | |||||
Average 400℃ | 0.08 | 0.08 | 0.08 | ||
Average 600℃ | 0.19 | 0.12 | 0.12 | ||
Average 800℃ | 0.19 | 0.16 | 0.16 | ||
Average 1000℃ | 0.23 | ||||
Chemical composition : | |||||
Al2O3 | 43 | 45 | 35 | 40 | 72 |
SiO2 | 55 | 52 | 46.7 | 58.1 | 28 |
ZrO2 | 15-17 | ||||
Cr2O3 | 1.8 |
Standard Dimension
Density: 96,128,160Kg/m3
Dimension:14400×610×13 mm 7200×610×25 mm 3600×610×50 mm