Semiconducting PE Jacketing Compound for High Voltage Cable
I. Type andapplication
Type | Product | Application |
EB-35A | Semiconducting PE Jacketing Compound for High Voltage Cable | Applying to high voltage cables and other area cables as jacketing compound |
EBZ-35A | Semiconducting flame retardant PE Jacketing Compound for High Voltage Cable | Applying to high voltage cables and other area cables as flame retardant jacketing compound |
II. Product description
These products used macromolecule PE materials as basematerials, and added other additivers. It is designed for high voltage cablesspecially, which suited to thin wall double co-extrusion processing conditionas thermoplastic semiconducting jacketing compound. It has very goodconductive, thermal conductivity, dispersivity, and excellent extrudingproperties, and etc.
III. Processing
Use single screwextruder to process, suggest to put one layer 60/80 strainer.
The followingtemperature(℃) profile of extruder is recommended:
Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Zone 5 | head | Die1 | Die2 | Die3 |
Temperature ℃ | 140 | 150 | 155 | 165 | 165 | 160 | 163 | 165 | 168 |
Note:Above information just for you refer, please adjust it according to equipmentconditions and extruding situation.
IV. Storage and transport
Packaging:25kg/bag,Aluminum foil vacuum and moistureproofinside bag and complex Kraft outside bag.
Storage and transport: Avoiding in directsunlight and weathering. The storage place should be in clean, cool, dry, andventilated conditions.
V. Properties
Table
Item | Unit | Standard Value | |
EB-35A | EBZ-35A | ||
Volume Resistivity, at 23℃ | ≤Ω﹒cm | 100 | 100 |
Melt Flowing Index | ≤g/10min | 1.0 | 1.0 |
Density | ≤g/cm3 | 1.15 | 1.25 |
Tensile Strength | ≥MPa | 13.0 | 12.0 |
Elongation at Break | ≥% | 400 | 400 |
Impact Brittleness in low temp. | ≤℃ | -45 | -45 |
Resistance to Environmental Stress Crack F0 | ≥h | 500 | 500 |
Oxygen Index | ≥ % | - | 28 |