Oil resistant PVCjacket compound
I. Type andapplication
Type | Product | Application and Cable Specification |
1372N | 70℃ Oil resistant PVC jacket compound | Jacket for oil resistant wires and cables which working voltage is 450/750V |
1392N | 90℃ Oil resistant PVC jacket compound | Jacket for oil resistant and heat resistant wires and cables which working voltage is 450/750V |
II. Productdescription
Oil resistant PVC jacket compound for wiresand cables, based on PVC resin, ismade into granula by mixing, plastification and granulation with addingplasticizer, stabilizing agent, anti-oxidant, butadiene-acrylonitrile rubber,pigment and etc.This product haswell performance of oil resistant. The products meetvarious special requirements, such as different hardness, UV stable,environment friend (RoHs, REACH, PAHs, chlorinated alkanes free, phthalate free, and etc.), sub-shine and fogsurface, low temperature resistant, PS/ABS transfer proof, rodent-repellent,termite-repellent, and etc.
III. Processing
It is recommended that compound should beprocessed with common extruder having a minimum L/D ratio of 20.
The following temperature(℃) profile of extruder is recommended
Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Head | Die |
Temperature ℃ | 140 | 160 | 165 | 170 | 170 | 170 |
IV. Storageand transport
Packaging：25kg/bag， PE membrane inside bag and Kraft outsidebag.
Storage and transport: Avoiding in directsunlight and weathering. The storage place should be in clean, cool, dry, andventilated conditions.
V. Properties
Table
Item | Unit | Standard Value | |
1372N | 1392N | ||
Tensile Strength | ≥ MPa | 12.5 | 12.0 |
Elongation at Break | ≥ % | 200 | 120 |
Impact Brittleness Temperature | ℃ | -40 | -20 |
Volume Resistivity, at 20℃ | ≥Ω﹒m | 1.0×108 | 1.0×108 |
Dielectric Strength | ≥ MV/m | 18 | 18 |
Thermal Stability Time at 200℃ | ≥ min | 50 | 80 |
Thermal Aging |
|
|
|
Aging Temperature | ℃ | 100±1 | 120±1 |
Aging Time | h | 168 | 120 |
Retention on Tensile Strength | ≥ % | 80 | 80 |
Retention on Elongation at Break | ≥ % | 70 | 70 |
Oil Resistant Test |
|
|
|
Test Temp. | ℃ | 90±2 | 90±2 |
Test Time | h | 24 | 24 |
Retention on Tensile Strength | ≥ % | 70 | 70 |
Retention on Elongation at Break | ≥ % | 70 | 70 |