High Quality Hollow Section-Square Tubes

Loading Port:China main port

Payment Terms:TT or L/C

Min Order Qty:5 m.t.

Supply Capability:1000 m.t./month

Product Description:

High Quality Hollow Section-Square Tubes

 

 

Product Applications:

It is widely used in building, machine, chemical equipment, automobile industrial, container, it is also applied to agriculture and mine machine.

 

Product Specifications:

Standards: ASTM A500, GB6728

Grade: ASTM A500: A, B, C; GB6728: Q195, Q215, Q235, Q345

  

Sizes:

*Remark: Besides below sizes, we also can arrange production based on requirement of customers

Size (mm)

Thickness (mm)

20×10

0.6-1.0

25×12

0.6-1.0

38×19

0.6-1.5

50×25

0.6-1.5

50×30

1.6-3.0

60×40

1.5-3.5

75×50

1.5-4.0

80×40

1.5-4.0

100×50

2.0-6.0

100×60

2.0-6.0

100×75

2.0-6.0

120×60

3.0-6.0

120×80

3.0-6.0

125×50

3.0-6.0

125×75

3.0-6.0

150×50

3.0-6.0

150×75

3.0-6.0

150×100

4.0-12

160×80

4.0-6.0

175×100

4.0-12

200×100

4.0-12

200×150

4.0-12

250×150

5.0-12

300×200

5.0-12

400×200

5.0-12

Chemical Composition:

Chemical Requirement

 

Composition %

 

Grade A

Grade B

 

Heat

Product

Heat

Product

Element

analysis

analysis

analysis

analysis

Carbon max

0.26

0.3

0.22

0.26

Manganese max

1.4

1.45

Phosphorus, max

0.035

0.045

0.03

0.04

Sulfur max

0.035

0.045

0.02

0.03

Copper, when copper steel is specified, min

0.2

0.18

0.2

0.18

Where an ellipsis (...)appears in this table, there is no requirement

For each reduction of 0.01 percentage point below the specified maximum for carton, and increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50% by heat analysis and 1.6% by product analysis

Mechanical Properties:

Tensile Requirement

 

Grade A

Grade B

Tensile strength, min, psi (Mpa)

48000 (400)

70000 (483)

Yield strength, min, psi (Mpa)

36000 (250)

50000 (345)

Elongation in 2 in. (50.8mm), min, %

23

23

 

GB6728:

Steel Grade

CHEMICAL COMPOSITION

MECHANICAL PROPERTIES

C (%)

Si (%)

Mn

(%)

P (%)

Max

S (%)

Max

YS (Mpa)

Min

TS (Mpa)

Min

El (%)

Min

Q195

0.06-0.012

0.3

0.25-0.5

0.45

0.5

195

315

22

Q215

0.09-0.15

0.3

0.25-0.55

0.45

0.5

215

335

22

Q235

0.12-0.22

0.3

0.3-0.7

0.45

0.45

235

375

20

Q345

0.20

0.55

1.0-1.6

0.45

0.45

345

510

21

Packaging: Packed in bundles, each bundle with 6-8 steel stripes and 2 nylon strips or one by one Or Nested into Containers

 

Product Images:

 

producing of Hollow Section-Square Tubes

 

 

Hollow Section-Square Tubes

 

 

High Quality Hollow Section-Square Tubes

 

 

High Quality Hollow Section-Square Tubes

 

FAQ:

Q1: Why buy Materials & Equipment from OKorder.com?

A1: All products offered byOKorder.com are carefully selected from China's most reliable manufacturing enterprises. Through its ISO certifications, OKorder.com adheres to the highest standards and a commitment to supply chain safety and customer satisfaction.

 

Q2: How do we guarantee the quality of our products?

A2: We have established an advanced quality management system which conducts strict quality tests at every step, from raw materials to the final product. At the same time, we provide extensive follow-up service assurances as required.

 

Q3: How soon can we receive the product after purchase?

A3: Within three days of placing an order, we will begin production. The specific shipping date is dependent upon international and government factors, but is typically 7 to 10 workdays.

 

Q4: What makes stainless steel stainless?

A4: Stainless steel must contain at least 10.5 % chromium. It is this element that reacts with the oxygen in the air to form a complex chrome-oxide surface layer that is invisible but strong enough to prevent further oxygen from "staining" (rusting) the surface. Higher levels of chromium and the addition of other alloying elements such as nickel and molybdenum enhance this surface layer and improve the corrosion resistance of the stainless material.

 

Q5: Can stainless steel rust?

A5: Stainless does not "rust" as you think of regular steel rusting with a red oxide on the surface that flakes off. If you see red rust it is probably due to some iron particles that have contaminated the surface of the stainless steel and it is these iron particles that are rusting. Look at the source of the rusting and see if you can remove it from the surface.

 

Q6: What is the difference between galvanized steel and galvalume steel?

A6: Galvanized steel is metallic coated with Zinc in various coating weights. Minimum recommended for painted metal roofs is G90. Galvalume is a zinc and aluminum coated steel that becomes an alloy and is recommended in either painted or bare applications with a minimum coating weight of AZ50. Galvalume has an excellent performance life in bare exposures. Hence if you are using a bare panel use galvalume and if painted use either.

 

Q7: Is there a difference in thermal conductivity between stainless steel and steel?

A6: Yes. Stainless Steel has a lower thermal conductivity rate than steel; approximately 1/3 to 1/5th depending on the material.

 

Q8: Is there a difference in electrical conductivity between stainless steel and steel?

A8: Yes. Steel is generally more conductive than stainless steel. Steel has resistivity in the range of 10~20Ωm, while stainless has a resistivity of approximately 60~72Ωm.