Loading Port:China Main Port
Payment Terms:TT OR LC
Min Order Qty:-
Supply Capability:-
1.Good acid and erosion resistance;
2.Widely used for different furnace;
3.Good bonding and structural strength of furnace.
Features:
1.Good acid and erosion resistance, powerful anti high-temperature strength.
2.Soften melting temperature is 1620~1670 °C.
3.Low thermal shock resistance.
4.Natural silica as raw material, plus regular mineralizer.
5.Ensure good bonding and structural strength of furnace.
6.Good heat resistance and long service life.
Application:
1.Glass melting furnace, ceramic frit kiln, sodium silicate furnace, soaking furnace, ceramic kiln, etc
2.Coke oven's coking chamber, combustion chamber walls, steel open-hearth's regenerator and sediment chamber, etc.
3.Load-bearing parts of high temperature hot air furnace and acid open-hearth furnace roof, etc.
Item | Properties | |||
BG-96A | BG-96B | BG-95A | BG-95B | |
SiO2,% | 96 | 96 | 95 | 95 |
Fe2O3 ,% | 0.8 | 1.0 | 1.2 | 1.2 |
Melt index,% Unit weight<20KG Unit weight≥20KG |
0.5 0.6 |
— — |
0.7 0.7 |
— — |
Cold Crushing strength MPa, Unit weight<2KG Unit weight≥20KG |
35(30) 30(25) | |||
Softening temperature under load,°C | 1680 | 1670 | 1660 | 1650 |
Apparent porosity % | 22(24) | |||
Bulk density,g/cm3 | 1.85-1.9 | |||
True density,g/cm3 | 2.34 | 2.35 | ||
Application | sodium silicate furnace,ceramic frit furnace ,glass furnace,coking furnace, metallurgical furnace and other furnaces | |||