Loading Port:Qingdao
Payment Terms:TT OR LC
Min Order Qty:300 m.t.
Supply Capability:2000 m.t./month
1.insulation rock wool
2.fiber glass tissue faced
3.easy to install
4.fire rating :Class A
5.waterproof and CE , ISO ce
Fiber glass tissue faced insulation Rock wool board (IB Series) have good strength and heat stability and chemical stability. Meanwhile, it has excellent sound absorption, heat preservation property and with A1 fire resistant class.
Then we can according to clients demand, produce waterproof and Low chloride rock wool and faced aluminum foil, glass cloth and so on facing material.
Item | IB60 | IB80 | IB100 | IB120 | IB150 |
Density | 60 | 80 | 100 | 120 | 150 |
Thickness | 40-150 | 25-150 | 25-150 | 25-120 | 25-100 |
Size (Length*Width) | 1200*600 | ||||
Item | IB60 | IB80 | IB100 | IB120 | IB150 | Unit | Standard | ||||||
Thermal Conductivity | 50℃ | ≤0.040 | ≤0.038 | ≤0.038 | ≤0.038 | ≤0.038 | W/(m.k) | GB/T 10295 | |||||
100℃ | ≤0.046 | ≤0.045 | ≤0.045 | ≤0.045 | ≤0.045 | ||||||||
150℃ | ≤0.060 | ≤0.058 | ≤0.056 | ≤0.055 | ≤0.055 | ||||||||
200℃ | ≤0.077 | ≤0.071 | ≤0.067 | ≤0.064 | ≤0.062 | ||||||||
250℃ | ≤0.095 | ≤0.085 | ≤0.080 | ≤0.074 | ≤0.070 | ||||||||
300℃ | ≤0.120 | ≤0.099 | ≤0.095 | ≤0.090 | ≤0.085 | ||||||||
Highest service temperature | 450 | 650 | 750 | 750 | 750 | ℃ | ASTMC411 | ||||||
Facing material | |||||||||||||
Thermal load shrinkage temperature | 400 | 600 | 650 | 650 | 650 | ℃ | GB/T11835 | ||||||
Linear Shrinkage | ≤2 | ≤2 | ≤2 | ≤2 | ≤2 | % | ASTMC356 | ||||||
Volume moisture absorption rate | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | Vol% | GB/T 5480 | ||||||
Hydrophobicity | ≥99 | ≥99 | ≥99 | ≥99 | ≥99 | % | |||||||
Chloride content | ≤10 | ≤10 | ≤10 | ≤10 | ≤10 | Ppm | ASTM C871 | ||||||
combustion performance | non-inflammable ,A1class | GB 8624 | |||||||||||
organic content | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | % | GB/T 11835 | ||||||
environmental | Non asbestos ,CFCs,HCFCs and HFCs | ----- | ----- | ||||||||||
corrosivity | non-corroding | ------ | ASTM C665
| ||||||||||